| HL-16 | HL-17 | H-18 | H-14 | HL-12 | HL-19 | ||
|---|---|---|---|---|---|---|---|
| 最高使用温度℃ | 1700 | 1700 | 1750 | 1400 | 1200 | 1100 | |
| 体积密度 g/cm3 | 110℃×24h | ≥2800 | ≤1750 | ≥3000 | ≥2400 | ≤1200 | ≤950 |
| 化学成份% | Al2O3%≤ | 93 | 93 | 95 | 60 | - | - |
| SiO2%≤ | 0.5 | 0.5 | 0.5 | - | - | - | |
| Fe2O3≤ | 0.7 | 0.7 | 0.7 | - | - | - | |
| CaO≤ | 5 | 5 | 4 | - | - | - | |
| 耐压强度≥ | 110℃×24h | 80 | 15 | 80 | 60 | 8 | 3.0 |
| 1000℃×24h | 80 | - | 80 | 60 | 5 | 2.5 | |
| 1200℃×24h | 80 | 12 | 80 | - | - | - | |
| 抗折强度≥ | 110℃×24h | 8 | 3 | 8 | 7 | 3 | 1.5 |
| 1000℃×24h | 8 | - | 8 | 7 | 2 | 1.0 | |
| 1200℃×24h | 8 | 2 | 8 | 7 | - | - | |
| 烧后线变化率%≤ | 1400℃×3h 0.4 | 1500℃×3h 0.3 | 1500℃×3h 0.5 | 1300℃×3h 0.4 | 800℃×3h 0.15 | 900℃×3h 0.4 | |
| 导热系数W/m.k≤ | - | 800℃ 0.7 | - | - | 500℃ 0.28 | 500℃ 0.26 | |